UHP 600x2400mm Graphite Electrodes for Electric Arc Furnace EAF
Technical Parameter
|
Parameter |
Part |
Unit |
UHP 600mm(24”) Data |
|
Nominal Diameter |
Electrode |
mm(inch) |
600 |
|
Max Diameter |
mm |
613 |
|
|
Min Diameter |
mm |
607 |
|
|
Nominal Length |
mm |
2200/2700 |
|
|
Max Length |
mm |
2300/2800 |
|
|
Min Length |
mm |
2100/2600 |
|
|
Max Current Density |
KA/cm2 |
18-27 |
|
|
Current Carrying Capacity |
A |
52000-78000 |
|
|
Specific Resistance |
Electrode |
μΩm |
4.5-5.4 |
|
Nipple |
3.0-3.6 |
||
|
Flexural Strength |
Electrode |
Mpa |
≥12.0 |
|
Nipple |
≥24.0 |
||
|
Young’s Modulus |
Electrode |
Gpa |
≤13.0 |
|
Nipple |
≤20.0 |
||
|
Bulk Density |
Electrode |
g/cm3 |
1.68-1.72 |
|
Nipple |
1.80-1.86 |
||
|
C.T.E. |
Electrode |
×10-6/℃ |
≤1.2 |
|
Nipple |
≤1.0 |
||
|
Ash Content |
Electrode |
% |
≤0.2 |
|
Nipple |
≤0.2 |
NOTE:Any specific requirement on dimension can be offered.
Product Characters
UHP graphite electrodes offer several advantages over traditional electrodes for EAF steel making. Their high thermal conductivity, low impurity content, longer lifespan, and consistent performance make them an ideal choice for steelmakers for a cost-effective, efficient, and eco-friendly solution.Moreover, UHP graphite electrodes provide an eco-friendly solution for steelmakers.
Ultra High Power(UHP) Graphite Electrode Current Carrying Capacity Parameter
| Nominal Diameter |
Ultra High Power(UHP) Grade Graphite Electrode |
||
|
mm |
Inch |
Current Carrying Capacity(A) |
Current Density(A/cm2) |
|
300 |
12 |
20000-30000 |
20-30 |
|
350 |
14 |
20000-30000 |
20-30 |
|
400 |
16 |
25000-40000 |
16-24 |
|
450 |
18 |
32000-45000 |
19-27 |
|
500 |
20 |
38000-55000 |
18-27 |
|
550 |
22 |
45000-65000 |
18-27 |
|
600 |
24 |
52000-78000 |
18-27 |
|
650 |
26 |
70000-86000 |
21-25 |
|
700 |
28 |
73000-96000 |
18-24 |
Surface Quality Ruler
- 1.The defects or holes should not more than two parts on the graphite electrode surface, and the defects or holes size not be allowed exceed the data in table below mentioned.
- 2.There is no transverse crack on the electrode surface.For longitudinal crack,its length should be not more than 5% of the graphite electrode circumference,its width should be within 0.3-1.0mm range.Longitudinal crack data below 0.3mm data should be negligible
- 3.The width of he rough spot(black) area on the graphite electrode surface should be not less than 1/10 of the graphite electrode circumference,and the length of rough spot(black) area over 1/3 of the graphite electrode length is not be allowed.
Surface Defect Data for Graphite Electrode
|
Nominal Diameter |
Defect Data(mm) |
||
|
mm |
inch |
Diameter(mm) |
Depth(mm) |
|
300-400 |
12-16 |
20–40 |
5–10 |
|
450-700 |
18-24 |
30–50 |
10–15 |
Related products
-
Furnace Graphite Electrode Small Diameter 75mm ...
Technical Parameter Chart 1:Technical Parameter For Small Diameter Graphite Electrode Diameter Part Resistance Flexural Strength Young Modulus Density C.T.E Ash Inch mm μΩ·m MPa GPa g/cm3 ×10-6/℃ % 3 75 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64 ≤2.4 ≤0.3 Nipple 5.8-6.5 ≥16.0 ≤13.0 ≥1.74 ≤2.0 ≤0.3 4 100 Electrode 7.5-8.5 ≥9.0 ≤9.3 1.55-1.64 ≤2.4 ≤0.3 Nip...
-
Graphite Electrodes With Nipples Manufacturers ...
Technical Parameter Parameter Part Unit HP 300mm(12”) Data Nominal Diameter Electrode mm(inch) 300(12) Max Diameter mm 307 Min Diameter mm 302 Nominal Length mm 1600/1800 Max Length mm 1700/1900 Min Length mm 1500/1700 Current Density KA/cm2 17-24 Current Carrying Capacity A 13000-17500 Specific Resistance Electrode μΩm 5.2-6.5 Nipple 3.5-4.5 Flexu...
-
Low Sulphur FC 93% Carburizer Carbon Raiser Iro...
Graphite Petroleum Coke (GPC) Composition Fixed Carbon(FC) Volatile Matter(VM) Sulphur(S) Ash Nitrogen(N) Hydrogen(H) Moisture ≥98% ≤1% 0≤0.05% ≤1% ≤0.03% ≤0.01% ≤0.5% ≥98.5% ≤0.8% ≤0.05% ≤0.7% ≤0.03% ≤0.01% ≤0.5% ≥99% ≤0.5% ≤0.03% ≤0.5% ≤0.03% ≤0.01% ≤0.5% Size: 0-0.50mm,5-1mm, 1-3mm, 0-5mm, 1-5mm, 0-10mm, 5-10mm, 5-10mm, 10-15mm or at customers’ option Packing:1.Waterproof...
-
Carbon Graphite Rod Black Round Graphite Bar Co...
Technical Parameter Item Unit Class Maximum particle 2.0mm 2.0mm 0.8mm 0.8mm 25-45μm 25-45μm 6-15μm Resistance ≤uΩ.m 9 9 8.5 8.5 12 12 10-12 Compressive strength ≥Mpa 20 28 23 32 60 65 85-90 Flexural strength ≥Mpa 9.8 13 10 14.5 30 35 38-45 Bulk density g/cm3 1.63 1.71 1.7 1.72 1.78 1.82 1.85-1.90 CET(100-600°C) ≤×10-6/°C 2.5 ...
-
Ultra High Power UHP 650mm Furnace Graphite Ele...
Technical Parameter Parameter Part Unit UHP 650mm(26”) Data Nominal Diameter Electrode mm(inch) 650 Max Diameter mm 663 Min Diameter mm 659 Nominal Length mm 2200/2700 Max Length mm 2300/2800 Min Length mm 2100/2600 Max Current Density KA/cm2 21-25 Current Carrying Capacity A 70000-86000 Specific Resistance Electrode μΩm 4.5-5.4 Nipple 3.0-3.6 Flexu...
-
Graphite Electrodes Dia 300mm UHP High Carbon G...
Technical Parameter Parameter Part Unit UHP 300mm(12”) Data Nominal Diameter Electrode mm(inch) 300(12) Max Diameter mm 307 Min Diameter mm 302 Nominal Length mm 1600/1800 Max Length mm 1700/1900 Min Length mm 1500/1700 Max Current Density KA/cm2 20-30 Current Carrying Capacity A 20000-30000 Specific Resistance Electrode μΩm 4.8-5.8 Nipple 3.4-4.0 F...